Temperature response of nanocellulose hydrogel from rubber wood

Abstract

This research investigates hydrogels derived from rubber wood waste's temperature responsiveness to nanocellulose-reinforced poly(N-isopropyl acrylamide) (PNIPAM) hydrogels. Nanocellulose was prepared via TEMPO-mediated oxidation for 6 hours and subsequently incorporated into PNIPAM hydrogels. Characterization by XRD, FT-IR, and ESEM confirmed the successful preparation of the nanocellulose. Further analysis of the nanocellulose hydrogels using UV-Vis, FE-SEM, and mechanical testing indicated that incorporating 0.10% w/v nanocellulose resulted in decreased light transmittance, reduced water absorption, enhanced mechanical strength, and improved thermal stability. Moreover, the nanocellulose hydrogels exhibited excellent and repeatable temperature responsiveness.

งานวิจัยนี้ศึกษาการตอบสนองต่ออุณหภูมิของไฮโดรเจลผสมนาโนเซลลูโลสที่ผลิตจากเศษไม้ยางพารา โดยเตรียมนาโนเซลลูโลสผ่านกระบวนการออกซิเดชันด้วยเทมโปเป็นเวลา 6 ชั่วโมง และนำไปเสริมแรงในไฮโดรเจล Poly(N-isopropylacrylamide) หรือ PNIPAM ผลการวิเคราะห์ด้วยเทคนิค XRD, FT-IR และ ESEM ของนาโนเซลลูโลสสามารถยืนยันถึงการมีอยู่ของเซลลูโลสที่มีขนาดนาโนเมตร วิเคราะห์นาโนเซลลูโลสไฮโดรเจลด้วยเทคนิค UV-Vis, FE-SEM และการทดสอบความแข็งแรงทางกล บ่งชี้ถึงนาโนเซลลูโลสไฮโดรเจล 0.10%w/v มีอัตราการส่องผ่านลดลง ลดการดูดซับน้ำ แข็งแรงมากขึ้น และมีความเสถียรต่อการเปลี่ยนแปลงของอุณหภูมิ นอกจากนี้ยังแสดงให้เห็นถึงความสามารถในการตอบสนองต่ออุณหภูมิซ้ำได้อย่างมีประสิทธิภาพ